Property Data for IE Series Polyurethane Product (Innovative Polymers)
 
 
Product
Mix Ratio Resin to Hardner by wt.
Mix ratio by Vol
Mixed Viscosity @77F 
Gel Time (min)
Color
Demold Time
Hardness
Tensile Strength ASTM D-638
Elongation at Break
Tear Strength ASTM D-624
Shrinkage (in/in)
Flex. Modulus ASTM D-790
Ultimate Flex. Strength ASTM D-790
Deflection Temp. ASTM D-648(66psi)
IE-10AH
100/100
100/100
600cps
10
Cream
10 hrs
5-10 A
150 psi
450%
25 pli
.001
N/A
N/A
N/A
IE-20AH
100/100
100/100
600cps
10
Cream
10 hrs
15-25 A
200 psi
175%
25 pli
.001
N/A
N/A
N/A
IE-35A
75/100
70/100
975cps
10-15
Clear
24 hrs
30-40 A
400 psi
470%
50 pli
.001
N/A
N/A
N/A
IE-50AC
50/100
47/100
975cps
10-15
Clear
24 hrs
45-50 A
600 psi
470%
60 pli
.001
N/A
N/A
N/A
IE-60A
25/100
22/100
975cps
20
Cream
10 hrs
55-65 A
2000 psi
470%
125 pli
.001
N/A
N/A
N/A
IE-70A
34/100
30/100
975cps
20
Cream
10 hrs
65-75 A
2000 psi
450%
200 pli
.005
N/A
N/A
N/A
IE-80A
35/100
32/100
975cps
20
Cream
8 hrs
75-85 A
2497 psi
296%
227 pli
.005
N/A
N/A
N/A
IE-90A
38/100
33/100
975cps
20
Cream
8 hrs
85-95 A
2500 psi
450%
250 pli
.005
N/A
N/A
N/A
IE-60DCD
100/12
100/13
2200cps
10
Clear Amber
2 hrs
45-50 D
2500 psi
200%
300 pli
.002
32500 psi
1400 psi
60degC
IE-65D
100/20
100/22
2000cps
15
Amber
2 hrs
55-55 D
2750 psi
250%
300 pli
.002
31000 psi
6800 psi
N/A
IE-68D
100/50
100/60
150cps
4-6
White
4 hrs
65-70 D
4900 psi
13%
500 pli
.003
180000 psi
7000 psi
65degC
IE-70D
100/50
100/60
200cps
20
White
24 hrs
70-75 D
6500 psi
8%
300 pli
.003
200000 psi
9000 psi
80degC
IE-70DC
100/50
100/55
1700cps
17-20
Clear
10 Hrs
65-75 D
4000 psi
60%
300 pli
.002
70000 psi
4500 psi
40degC
IE-80D
100/100
87/100
400cps
15-20
White
2-8 Hrs
70-80 D
10100 psi
7.5%
N/A
.002
325000 psi
13500 psi
60degC
 
 